PENOSIL PREMIUM FIRERATED GUNFOAM B1

Diversity is only limited by imagination

logo2 logo1

MATERIALS:

One-component professional fire-resistant foam with a structure of 70% / 30% (closed cells / open cells) and low expansion, supplied in cans with aerosol
Light pink color
Available in summer version
Adheres well to many building materials, except: Teflon, polyethylene and silicone surfaces
Provides very good sound and thermal insulation
Class B-s1, d0 reaction to fire acc. PN-EN 13501-1+A1:2010.

INSTALLATION:

The surface on which the application is made must be free of dust, dirt and oil
The surface on which the application will be made should be well moistened. Lack of adequate humidity can cause secondary expansion
Used for gaps or linear joints up to 50 mm wide
Applied on substrates of at least A2 reaction to fire
When applying in low temperatures, the can with foam should be preheated in a warm place or water. Place or water temperature should not exceed + 30 ° C
Before use, shake the can with foam vigorously at least 20 times
The amount of foam discharged should be adjusted with use of the injection gun trigger.
After curing, the foam is not UV-resistant and must be covered within 24 hours. Unprotected foam gets brittle. The foam can be painted with water-based paints
Dirt from foam can be cleaned with Premium Foam Cleaner, Premium Foam Remover or with Premium Cleaning Wipes. Details are given in the cards of these products
Detailed information on storage, transport and safety are available in the safety data sheet (SDS).

Properties	Unit	Value
Tack free time	minute	12-16
Cutting time (30 mm strap)	minute	30-40
Cutting time (30 mm strap)°C)	hour	up to 18
Completely cured in joint (in temperature +5 °C)	hour	up to 24
Density	kg/m³	25-30
Fire-resistance of cured foam (PN-EN 13501-2:2010 )		EI15 - EI120
Fire class of cured foam (PN-EN 13501-1+A1:2010 )	-	B-s1,d0
Volume decrease	%	non
Post-expansion	%	up to 30
Flash point of cured foam	°C	400
Tensile strength (BS 5241 )	N/cm²	8
Compression strength at 10% deformation (DIN 53421 )	N/cm²	2,5
Thermal conductivity	W/m*K	0,034
Temperature resistance of cured foam	°C	long period: -50 to +90
The following values were obtained at temperature +23°C and 50% relative humidity, unless stated otherwise.